Item Affected: SUSPENSION:REAR:AXLE:NON-POWERED AXLE ASSEMBLY
Date Announced: 06/22/2017
Description of Recall:
Conequence:
Action Need To Fix It:
Notes: PORTABLE ASPHALT PLANT. MANFD 1-1 1960 THRU 7-31 1962. POSSIBILITY THATINDUCTION HARDENING PROCESS AT NORTH AMERICAN ROCKWELL'S AXLE PLANT MAY HAVECREATED HIGH RESIDUAL STRESSES AT INNER BEARING SHOULDER AREA. STRESSES MAYTURN INTO PHYSICAL CRACKS UNDER EXTENDED FIELD SERVICE. CONTINUED USE OF AXLEAFTER CRACKING HAS OCCURED MAY CAUSE AXLE SPINDLE TO FRACTURE. (CORRECT BYINSPECTING AND REPLACING WHERE NECESSARY. )
Item Affected: SUSPENSION:REAR:AXLE:NON-POWERED AXLE ASSEMBLY
Date Announced: 06/22/2017
Description of Recall:
Conequence:
Action Need To Fix It:
Notes: PORTABLE ASPHALT PLANT. MANFD 1-1 1960 THRU 7-31 1962. POSSIBILITY THATINDUCTION HARDENING PROCESS AT NORTH AMERICAN ROCKWELL'S AXLE PLANT MAY HAVECREATED HIGH RESIDUAL STRESSES AT INNER BEARING SHOULDER AREA. STRESSES MAYTURN INTO PHYSICAL CRACKS UNDER EXTENDED FIELD SERVICE. CONTINUED USE OF AXLEAFTER CRACKING HAS OCCURED MAY CAUSE AXLE SPINDLE TO FRACTURE. (CORRECT BYINSPECTING AND REPLACING WHERE NECESSARY. )
Item Affected: SUSPENSION:REAR:AXLE:NON-POWERED AXLE ASSEMBLY
Date Announced: 06/22/2017
Description of Recall:
Conequence:
Action Need To Fix It:
Notes: PORTABLE ASPHALT PLANT. MANFD 1-1 1960 THRU 7-31 1962. POSSIBILITY THATINDUCTION HARDENING PROCESS AT NORTH AMERICAN ROCKWELL'S AXLE PLANT MAY HAVECREATED HIGH RESIDUAL STRESSES AT INNER BEARING SHOULDER AREA. STRESSES MAYTURN INTO PHYSICAL CRACKS UNDER EXTENDED FIELD SERVICE. CONTINUED USE OF AXLEAFTER CRACKING HAS OCCURED MAY CAUSE AXLE SPINDLE TO FRACTURE. (CORRECT BYINSPECTING AND REPLACING WHERE NECESSARY. )
Item Affected: SUSPENSION:REAR:AXLE:NON-POWERED AXLE ASSEMBLY
Date Announced: 06/22/2017
Description of Recall:
Conequence:
Action Need To Fix It:
Notes: PORTABLE ASPHALT PLANT. MANFD 1-1 1960 THRU 7-31 1962. POSSIBILITY THATINDUCTION HARDENING PROCESS AT NORTH AMERICAN ROCKWELL'S AXLE PLANT MAY HAVECREATED HIGH RESIDUAL STRESSES AT INNER BEARING SHOULDER AREA. STRESSES MAYTURN INTO PHYSICAL CRACKS UNDER EXTENDED FIELD SERVICE. CONTINUED USE OF AXLEAFTER CRACKING HAS OCCURED MAY CAUSE AXLE SPINDLE TO FRACTURE. (CORRECT BYINSPECTING AND REPLACING WHERE NECESSARY. )